| Home |
| Tapes |
| ABS |
| Acetals |
| Acrylic |
| Acetate-CAB |
| Carbon
Fiber |
| CPVC |
| ECTFE-
Halar® |
| Ertalyte
Petp |
| ETFE |
| EVA |
| FEP
Fluoropolymers |
| Fiberglass-FRP |
| Fluorosint® |
| G10/FR4,
LE, CE, XX, G7, G5, G11
Phenolics |
| Graphite |
| HDPE |
| HIPS-Polystyrene |
| Kevlar |
| LDPE |
| LLDPE-Linear
Low |
| MDPE |
| Neoprene |
| Noryl® |
| Nylon |
| Nylatron® |
| PBT |
| PCTFE |
| Peek |
|
Petg
|
| PFA-Fluropolymer |
|
Polycarbonate
|
| Polyester |
| Polyimide-
Cirlex, Pyropel, Vespel |
|
Polypropylene
|
| Polystyrene |
| Polysulfone |
| Polyurethane-TPU |
| PTFE |
| PVC |
| PVDF |
| Rubber |
| Rulon |
| Santoprene® |
| Silicone |
| Teflon® |
| Torlon® |
| TPX |
| Tygon® |
| UHMWPE |
| Ultem®
PEI |
| Versilic®
|
| Zelux®
|
| Contact
Excel Plastics
|
| Domestic
Selling Policy
|
| Metal
Steel Balls
|
|
HDPE
Colored Sheets
Tapes
Acrylic Colored Pig
Pipes
Circuit
Breakers
Murray
Circuit Breakers
Pinewood Derby Cars
Texas Longhorns
Metal
Sheets, Rods, Tubes, Bars
|
| |
TIVAR® UV RESISTANT
- For outdoor applications
- Retains key properties up to three times longer
Modified TIVAR® formula for enhanced
stability in outdoor applications. While non-UV formulations are suitable for
unexposed situations, TIVAR® UV Resistant retains its low-friction
surface, resistance to wear, corrosion resistance and impact strength up to
three times longer.
TIVAR® UV Resistant is available in sheet.
Technical Specification Table
| Property |
Method |
SI Unit |
SI Value |
| Density |
ASTM D-792 |
g/cm3 |
0.953 |
| Yield Point |
ASTM D-638 |
MPa |
20 |
| Elongation at Yield |
ASTM D-638 |
% |
15 |
| Tensile Break |
ASTM D-638 |
MPa |
45 |
| Elongation at Break |
ASTM D-638 |
% |
290 |
| Tensile Modulus |
ASTM D-638 |
MPa |
913 |
| Flexural Modulus |
ASTM D-790 |
MPa |
723 |
| Izod Impact (Charpy Notched Impact) |
ASTM D-4020 |
kJ/m2 |
113 |
| Tensile Impact |
DIN 53448 |
kJ/m2 |
3096 |
| Sand Wheel Wear |
ASTM G-65 |
T-1000=100 |
113 |
| Hardness |
ASTM D-2240 |
Shore D |
69 |
| Static Friction |
ASTM D-1894 |
Unitless |
0.18 |
| Dynamic Friction |
ASTM D-1894 |
Unitless |
0.15 |
| Coefficient of Thermal Exp |
ASTM D-696 |
°C-1 |
0.00018 |
| Melt Point |
ASTM D-3417 |
°C |
137-143 |
| Compressive Modulus |
ASTM D-695 |
MPa |
na |
| Compressive Deformation |
ASTM D-621 |
% at 454.5kg |
na |
| Volume Resistivity |
ASTM D-257 |
Ohm-cm |
>1015 |
| Surface Resistivity |
ASTM D-257 |
Ohm |
>1015 |
| Water Absorption |
ASTM D-5706 |
% |
nil |
| |
|