| Home |
| Tapes |
| ABS |
| Acetals |
| Acrylic |
| Acetate-CAB |
| Carbon
Fiber |
| CPVC |
| ECTFE-
Halar® |
| Ertalyte
Petp |
| ETFE |
| EVA |
| FEP
Fluoropolymers |
| Fiberglass-FRP |
| Fluorosint® |
| G10/FR4,
LE, CE, XX, G7, G5, G11
Phenolics |
| Graphite |
| HDPE |
| HIPS-Polystyrene |
| Kevlar |
| LDPE |
| LLDPE-Linear
Low |
| MDPE |
| Neoprene |
| Noryl® |
| Nylon |
| Nylatron® |
| PBT |
| PCTFE |
| Peek |
|
Petg
|
| PFA-Fluropolymer |
|
Polycarbonate
|
| Polyester |
| Polyimide-
Cirlex, Pyropel, Vespel |
|
Polypropylene
|
| Polystyrene |
| Polysulfone |
| Polyurethane-TPU |
| PTFE |
| PVC |
| PVDF |
| Rubber |
| Rulon |
| Santoprene® |
| Silicone |
| Teflon® |
| Torlon® |
| TPX |
| Tygon® |
| UHMWPE |
| Ultem®
PEI |
| Versilic®
|
| Zelux®
|
| Contact
Excel Plastics
|
| Domestic
Selling Policy
|
| Metal
Steel Balls
|
|
HDPE
Colored Sheets
Tapes
Acrylic Colored Pig
Pipes
Circuit
Breakers
Murray
Circuit Breakers
Pinewood Derby Cars
Texas Longhorns
Metal
Sheets, Rods, Tubes, Bars
|
| |
| Celazole Technical Data |
| Physical Properties |
Metric |
English |
Comments |
|
|
|
|
|
|
| Density |
1.3 g/cc |
0.047 lb/in³ |
ISO 1183 |
| Water Absorption |
0.5 % |
0.5 % |
24 hour immersion; ISO
62 |
| Water Absorption |
1.06 % |
1.06 % |
96 hour immersion; ISO
62 |
Mechanical Properties |
|
|
| Tensile Strength, Ultimate |
160 MPa |
23200 psi |
ISO 527 |
| Elongation at Break |
3 % |
3 % |
ISO 527 |
| Tensile Modulus |
5.8 GPa |
841 ksi |
ISO 527 |
| Compressive Yield Strength |
42 MPa |
6090 psi |
at 1% nominal strain;
ISO 604 |
| Compressive Yield Strength |
82 MPa |
11900 psi |
at 2% nominal strain;
ISO 604 |
| Charpy Impact, Notched |
0.35 J/cm² |
1.67 ft-lb/in² |
ISO 179/1eA |
Electrical Properties |
|
|
| Electrical Resistivity |
1e+014 ohm-cm |
1e+014 ohm-cm |
IEC 93 |
| Surface Resistance |
Min 1e+012 ohm |
Min 1e+012 ohm |
IEC 93 |
| Dielectric Constant |
3.3 |
3.3 |
1 MHz; IEC 250 |
| Dielectric Constant, Low Frequency |
3.3 |
3.3 |
100 Hz; IEC 250 |
| Dielectric Strength |
22 kV/mm |
559 kV/in |
IEC 243 |
| Dissipation Factor, Low Frequency |
0.001 |
0.001 |
100 Hz; IEC 250 |
Thermal Properties |
|
|
| CTE, linear 20°C |
25 µm/m-°C |
13.9 µin/in-°F |
average value between
23 and 100°C |
| CTE, linear 100°C |
25 µm/m-°C |
13.9 µin/in-°F |
average value between
23 and 150°C |
| Thermal Conductivity |
0.4 W/m-K |
2.78 BTU-in/hr-ft²-°F |
|
| Maximum Service Temperature, Air |
310 °C |
590 °F |
20,000 hours continuous |
| Maximum Service Temperature, Air |
500 °C |
932 °F |
for short periods |
| Deflection Temperature at 1.8 MPa
(264 psi) |
425 °C |
797 °F |
ISO 75 method A |
| Flammability, UL94 |
V-0 |
V-0 |
1.5 mm thickness |
| Flammability, UL94 |
V-0 |
V-0 |
3 mm thickness |
| Oxygen Index |
58 % |
58 % |
ISO 4589 |
|
|
| |
|